BASF Ultramid? B3EG6 PA6 GF30(尼龍6-聚酰胺)
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質(zhì)
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
Density密度
|
1.36 g/cc
|
0.0491 lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
6.3 - 6.9 %
|
6.3 - 6.9 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
1.9 - 2.3 %
|
1.9 - 2.3 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Test
|
140 cm3/g
|
140 cm3/g
|
Viscosity number; ISO 307
|
|
Linear Mold Shrinkage線性收縮率
|
0.0035 cm/cm
|
0.0035 in/in
|
|
|
Melt Flow熔體流動速率
|
68 g/10 min
@Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力學(xué)性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
Tensile Strength, Yield屈服拉伸強(qiáng)度
|
185 MPa
|
26800 psi
|
50mm/min; ISO 527
|
|
Elongation at Yield屈服伸長率
|
3.5 %
|
3.5 %
|
50mm/min; ISO 527
|
|
Modulus of Elasticity彈性模量
|
9.50 GPa
|
1380 ksi
|
ISO 527
|
|
Flexural Strength彎曲強(qiáng)度
|
270 MPa
|
39200 psi
|
ISO 178
|
|
Flexural Modulus彎曲彈性模量
|
8.60 GPa
|
1250 ksi
|
ISO 178
|
|
Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度 (ISO)
|
15.0 kJ/m2
|
7.14 ft-lb/in2
|
ISO 180/A
|
|
Charpy Impact Unnotched夏比缺口試樣沖擊
|
9.50 J/cm2
|
45.2 ft-lb/in2
|
ISO 179/1eU
|
|
8.00 J/cm2
@Temperature -30.0 °C |
38.1 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eU
|
|
|
Charpy ImPAct, Notched夏比缺口沖擊
|
1.50 J/cm2
|
7.14 ft-lb/in2
|
ISO 179/1eA
|
|
1.10 J/cm2
@Temperature -30.0 °C |
5.24 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eA
|
|